Jul 09, 2013 0183 32Grade Ti4.5Al3V2Mo2Fe alloy is an alphabeta alloy that is betarich with a fine microstructure and excellent superplastic formability. The following sections will discuss in detail about grade Ti4.5Al3V2Mo2Fe alloy.50
Technical Data North American Alloys
Ti4.5Al3V2Mo2Fe SP 700 SP 700 is an alpha beta alloy developed for superior super plastic forming properties. It is heat treatable with good strength and cold formability.
Mechanical properties of Ti4.5Al3V2Mo2Fe and ...
May 01, 2005 0183 32The balance of specific strength and fatigue ratio of singleannealed Ti4.5Al3V2Mo2Fe is around 210260 MPa/ g cm 3 and 0.800.85 MPa/MPa, respectively, which is better than other titanium alloys. This high balance in specific strength and fatigue ratio is supported by a modest ductility 1320 and modest fracture toughness 2535 kN/m .Cited by: 12
Titanium Ti4.5Al3V2Mo2Fe SP700
Titanium Ti4.5Al3V2Mo2Fe SP700 , Characteristics: Alphabeta alloy, betarich, fine microstructure, excellent superplastic formability. Appli ions: Aerospace components, metal wood heads, metal balloons, tools, automotive components, wrist
Integ Metals Titanium AlphaBeta
Ti4.5Al3V2Mo2Fe Titanium Alloy has very limited weldability . Machinability . Ti4.5Al3V2Mo2Fe Titanium is not best suited to machining. The best results are achieved using slow speeds, accurate cooling flow and high feed rates. Contact us now for more info and pricing.
Improvement in fracture toughness of Ti4.5Al3V2Mo2Fe ...
10 0183 32In order to improve the observed low fracture toughness of rich type Ti4.5Al3V2Mo2Fe annealed at the temperature of 1123 K, a twostep cooling TSC after solution treatment at that temperature was proposed instead of air cooling. Solution treatment plus aging STA and slow furnacecooling SFC treatments were also carried out on the same alloy for comparison. It was found that ...