Copper UNS C15500 AZoM.com

UNS C15500 copper has very good hot and cold workability, good forgeability, and good to excellent corrosion resistance. It can be fabricated by coining, drawing and upsetting, hot forging and pressing, swaging, coppersmithing, stamping, and spinning. The following datasheet provides more details about UNS C15500 copper.

Copper, UNS C15500, Quarter Hard

Copper, UNS C15500, Quarter Hard, Good to excellent corrosion resistance. Excellent hot and cold workability good forgeability. Fabricated by coining, coppersmithing ...

CDA COPPER NO. C 155 00 / SuperSilverCopper155TM

Hot Forgeability Rating Forging Brass 100 Hot Working Temperature 1,4001,600F or 750875C Annealing Temperature 7501,000F or 400540C Machinability Rating Free Cutting Brass 100 20 Suitability for being joined by: Soldering Excellent Brazing Excellent For other methods of joining, consult our Technical Services Group. 1,980F ...

Copper.org C15500 Alloy

Thermal Conductivity Btu/ sq ft/ ft hr/ F at 68F. 200. Coefficient of Thermal Expansion 68212 10 to 6 power per F 68 212F 9.8. Specific Heat Capacity Btu/ lb /F at 68F. 0.092. Modulus of Elasticity in Tension ksi. 17000. Modulus of Rigidity ksi.

Copper, UNS C15500, H01 Quarter Hard Temper

Copper, UNS C15500, H01 Quarter Hard Temper, Good to excellent corrosion resistance. Excellent hot and cold workability good forgeability. Fabricated by coining, coppersmithing, drawing and upsetting, hot forging and pressing, spinning, swaging

C15500

C15500 Millard Wire amp Specialty Strip Co. 449 Warwick Industrial Drive Warwick, RI 02886 Phone: 401 7379330 Fax: 401 7379340 Chemical Composition max., unless shown as range or min. Applicable Specifications Common Fabrication Processes Bending, Blanking, Drawing, Etching, Forming, Machining, Shearing, Spinning

UNS C15500 SilverBearing Copper :: MakeItFrom.com

Among wrought copper alloys, the composition of C15500 copper is notable for including magnesium Mg and silver Ag. Magnesium is used to improve strain hardenability. This increases strength but reduces the ability to form the alloy into complex shapes. Silver is used to increase recrystallization temperature in copper alloys.

C14500 Tellurium Copper Forging

C14500 Tellurium Copper Forging Tellurium copper is a kind of tellurium bronze material, the American ASTM standard grade is C14500. C14500 tellurium copper is a kind of highconducting easy cutting copper alloy material developed successfully in the 1960s in the United States according to its industrial development requirements.

Highperformance copperalloy wire

CuMg0.1 KY6 C15500 CuMg0.2 KY8 CW127C Bronze CuSn4 B03 CW450K C51100 CuSn5 B05 CW451K C51000 ... tips are frequently manufactured by cold forging for

PRE Post:3.7144 alloy italy
NEXT Post:0.0015 aluminium uganda

Changzong copper aluminium and alloy

2.4688 alloy oman

0.6 aluminium egypt

copper 678 cameroon

aluminium alloy sheet denmark

Copyright © .Changzong copper aluminium and alloy Industry Co.,Ltd All Rights Reserved.


Technical Support : Qianxing